风琴状

Organoid material

HF处理

HFTreatment

风琴状材料，由氢氟酸刻蚀得到。

Organ-like material obtained by etching withHF.

黏土材料

Clay materials

LiF处理

LiFTreatment

黏土材料，经超声离心可分散为单层材料，产率约为25-35%。超声功率需160W以上，时间约为2h到6h。

Clay material, which can be dispersed as a single layer material by ultrasonic centrifugation, yields about 25-35%. Ultrasound power needs more than 160W, and the time is about 2 h to 6 h.

单/少层胶体溶液

Single/Layer Colloidal Solution

5mg/ml

100ml

单/少层村料的胶体溶液，具有丁达尔现象，可以直接利用的MXenes材料。

The colloidal solution of single/few layer village material that has Tindal phenomenon and can be used directly.

单/少层胶体溶液

Single/Layer Colloidal Solution

10mg/ml

100ml

单/少层村料的胶体溶液，具有丁达尔现象，可以直接利用的MXenes材料。

The colloidal solution of single/few layer village material that has Tindal phenomenon and can be used directly.

单/少层粉末材料

Single/Layer Powder Material

冷冻干燥

freeze drying

单/少层村料的胶体溶液，经过冷冻干燥得到的粉末。

Powder obtained by freeze-drying of colloidal solution of single/small layer village material.

自支撑膜材料

Self-supporting membrane materials

真空抽滤

Vacuum suction filtration

单/少层村料的胶体溶液，经过真空抽滤得到的柔性膜。Flexible membranes obtained from the colloidal solution of single/small-layer village materials by vacuum filtration.